Damage and Fracture of Ceramic-Matrix Composites Under Stochastic Loading

Longbiao Li (Autor)

Buch | Softcover

197 Seiten

2022 | 1st ed. 2021
Springer Verlag, Singapore
978-981-16-2143-7 (ISBN)

Artikel merken

This book presents the relationships between tensile damage and fracture, fatigue hysteresis loops, stress-rupture, fatigue life and fatigue limit stress, and stochastic loading stress. Ceramic-matrix composites (CMCs) possess low material density (i.e., only 1/4 - 1/3 of high-temperature alloy) and high-temperature resistance, which can reduce cooling air and improve structure efficiency. Understanding the failure mechanisms and internal damage evolution represents an important step to ensure reliability and safety of CMCs. This book investigates damage and fracture of fiber-reinforced ceramic-matrix composites (CMCs) subjected to stochastic loading, including: (1) tensile damage and fracture of fiber-reinforced CMCs subjected to stochastic loading; (2) fatigue hysteresis loops of fiber-reinforced CMCs subjected to stochastic loading; (3) stress rupture of fiber-reinforced CMCs with stochastic loading at intermediate temperature; (4) fatigue life prediction of fiber-reinforced CMCssubjected to stochastic overloading stress at elevated temperature; and (5) fatigue limit stress prediction of fiber-reinforced CMCs with stochastic loading. This book helps the material scientists and engineering designers to understand and master the damage and fracture of ceramic-matrix composites under stochastic loading.

Dr. Longbiao Li is a lecturer in the College of Civil Aviation at the Nanjing University of Aeronautics and Astronautics. Dr. Li’s research focuses on the vibration, fatigue, damage, fracture, reliability, safety, and durability of aircraft and aero engine. In this research area, he is the first author of 162 SCI journal publications, 5 monographs, 2 edited books, 3 textbooks, 3 book chapters, 20 Chinese patents, 2 US patents, and more than 20 refereed conference papers. He has been involved in different projects related to structural damage, reliability, and airworthiness design for aircraft and aero engines, supported by the Natural Science Foundation of China, COMAC Company, and AECC Commercial Aircraft Engine Company.

Tensile Damage and Fracture of Ceramic-Matrix Composites subjected to Stochastic Loading.- Hysteresis Loops of Ceramic-Matrix Composites subjected to Stochastic Loading.- Stress-rupture of Ceramic-Matrix Composites under Stochastic Loading at Intermediate Temperature.- Fatigue Life of Ceramic-Matrix Composites subjected to Stochastic Loading at Elevated Temperature.- Fatigue Damage and Fracture of Ceramic-Matrix Composites subjected to Stochastic Loading.

Erscheinungsdatum	13.06.2022
Reihe/Serie	Advanced Ceramics and Composites ; 2
Zusatzinfo	98 Illustrations, color; 5 Illustrations, black and white; XI, 197 p. 103 illus., 98 illus. in color.
Verlagsort	Singapore
Sprache	englisch
Maße	155 x 235 mm
Themenwelt	Technik ► Fahrzeugbau / Schiffbau
	Technik ► Luft- / Raumfahrttechnik
	Technik ► Maschinenbau
Schlagworte	Ceramic-matrix composites (CMCs) • Fatigue Life • Fatigue limit stress • Fibers failure • Hysteresis loops • Interface debonding • Matrix Cracking • Stochastic loading • Stress-rupture
ISBN-10	981-16-2143-8 / 9811621438
ISBN-13	978-981-16-2143-7 / 9789811621437
Zustand	Neuware